Glass Fiber Reinforced Polyamide 6 (PA6 GF30 - P1288)

High-performance PA6-GF30 compound
30% glass fiber reinforced polyamide 6 (PA6), specifically designed for injection molding applications. Offers outstanding mechanical strength, dimensional stability, and heat resistance, making it ideal for:

Automotive components
Electrical housings
Technical and industrial parts

Key Properties

Tensile Strength: 176 MPa
Tensile Modulus: 1373 MPa
Flexural Modulus: 7462 MPa
Flexural Strength: 261 MPa
Impact Resistance:
  • Izod notched (23°C): 16.5 kJ/m²
  • Charpy notched (23°C): 11.2 kJ/m²
Melting Temperature: 198.4°C
Heat Deflection Temp (HDT, 1.8 MPa): 216.8°C
Flammability: UL94 HB

Processing Guidelines

Recommended Melt Temperature: 250–275°C
Mold Shrinkage: 0.2–0.6%
Pre-drying: 80–100°C for 4–8 hours

Full technical datasheet available upon request.